Our Stainless Steel Hot Rolled Annealed and Pickled (HRAP) Sheets and Plates are available in grades 304, 304L, and 316L, providing excellent corrosion resistance and strength for a variety of applications. With thickness options ranging from 3 mm to 8 mm and widths of 1250mm, 1500mm, and 1600mm, these sheets are ideal for industries such as construction, automotive, and manufacturing.
| Grade | Thickness (mm) | Width (mm) |
|---|---|---|
| 304 | 3 mm to 8 mm | 1250, 1500, 1600 |
| 304L | 3 mm to 8 mm | 1250, 1500, 1600 |
| 316L | 3 mm to 8 mm | 1250, 1500, 1600 |
Key Features:
- Grades: 304, 304L, and 316L, offering versatility for different environmental conditions.
- Thickness Range: From 3 mm to 8 mm, suitable for both structural and aesthetic applications.
- Widths: Available in 1250mm, 1500mm, and 1600mm for flexibility in design and manufacturing.
- Surface Finish: Hot rolled and annealed for enhanced durability and a smooth finish.
| Specification | Details |
|---|---|
| Material Grades | 304, 304L, 316L |
| Thickness Range | 3 mm to 8 mm |
| Width Options | 1250 mm, 1500 mm, 1600 mm |
| Length Options | Custom lengths available upon request |
| Surface Finish | Hot Rolled, Annealed, Pickled |
| Standard Compliance | ASTM A240, ASTM A480 |
| Tensile Strength | Varies by grade; typically: |
| 304: 520 MPa (min) | |
| 316L: 480 MPa (min) | |
| Yield Strength | Varies by grade; typically: |
| 304: 205 MPa (min) | |
| 316L: 290 MPa (min) | |
| Elongation | Varies by grade; typically: |
| 304: 40% (min) | |
| 316L: 40% (min) | |
| Hardness | Rockwell B Scale (RB) < 90 |